Efecto de la temperatura en la cristalización de películas de perovskita-ch3 nh3 pbi3 -xclx

Contenido principal del artículo

Daniel Cabrera

Resumen

In the present manuscript, the effect of temperature on crystallisation of perovskite
thin films (CH3NH3PbI3-xClx) was analysed (perovskite films are utilized
to produce perovskite-based solar cells that appear to be devices with lower production costs and higher efficiency than silicon-based solar cells). To synthesise the perovskite films, four samples with precursor solution were spin coated for 45 s at 2000 rpm. After that, the samples were annealed at three different temperatures. Likewise, samples were characterised by UV/Vis Spectroscopy, Emission Spectroscopy, Fluorescence Microscopy, and ImageJ
software were used to analyse crystal size. It was found that the sample annealed at 80 oC presented the highest fluorescence emission with 49539.09 CPS and the best particle size distribution. Band Gap Energy (Eg) was also calculated resulting in 1.60 ± 0.01 eV (An ideal solar cell has a band gap of 1.4 eV to absorb the maximum number of photons from the solar radiation).

Descargas

Los datos de descargas todavía no están disponibles.

Detalles del artículo

Cómo citar
Cabrera, D. (2022). Efecto de la temperatura en la cristalización de películas de perovskita-ch3 nh3 pbi3 -xclx. Alimentos Ciencia E Ingeniería, 28(2), 61–67. https://doi.org/10.31243/aci.v28i2.1636
Sección
Artículos

Citas

Lewis, N. S. (2007). Toward cost-effective
solar energy use. science,
315(5813), 798-801.
Ponseca Jr, C. S., Tian, Y., Sundström, V., & Scheblykin, I. G. (2016). Excited state and charge-carrier dynamics in perovskite solar cell materials. Nanotechnology, 27(8), 082001.
Yang, L., Barrows, A. T., Lidzey, D. G., & Wang, T. (2016). Recent progress and challenges of organometal halide
perovskite solar cells. Reports on Progress in Physics, 79(2), 026501.
Kojima, A., Teshima, K., Shirai, Y., & Miyasaka,
T. (2009). Organometal halide perovskites as visible-light sensitizers
for photovoltaic cells. Journal of the American Chemical Society, 131(17), 6050-6051.Nicole R. Title of paper with only first word capitalized.
J Name Stand Abbrev. In press.
Liu, J., Lin, J., Xue, Q., Ye, Q., He, X., Ouyang,
L., & Lau, W. M. (2016). Growth
and evolution of solution-processed
CH 3 NH 3 PbI 3-x Cl x layer for highly efficient planar-heterojunction
perovskite solar cells. Journal of Power Sources, 301, 242-250.Young M. Technical Writer’s Handbook. Mill Valley, CA: University Science;1989.
Huang, J., Wang, M., Ding, L., Deng, J., & Yao, X. (2015). Efficiency enhancement
of the MAPbI3? xClx-based perovskite solar cell by a two-step annealing procedure. Semiconductor Science and Technology, 31(2), 025009.
Dharma, J., Pisal, A., & Shelton, C. T. (2009). Simple method of measuring
the band gap energy value of TiO2 in the powder form using a UV/Vis/NIR spectrometer. Application
Note Shelton, CT: PerkinElmer.
Colella, S., Mosconi, E., Fedeli, P., Listorti,
A., Gazza, F., Orlandi, F., ... & Gigli, G. (2013). MAPbI3-xCl x Mixed Halide Perovskite for Hybrid
Solar Cells: The Role of Chloride
as Dopant on the Transport and Structural Properties. Chemistry of Materials, 25(22), 4613-4618.
Noh, J. H., Im, S. H., Heo, J. H., Mandal, T. N., & Seok, S. I. (2013). Chemical
management for colorful, efficient,
and stable inorganic–organic hybrid nanostructured solar cells. Nano letters, 13(4), 1764-1769